DURMAT^®

C

Si

Cr

Ni

Mo

Nb

V

B

Co

Fe

+

Hardness

(HRC)

33 PTA

–

4.1

6

Bal.

–

–

–

1

–

<3

–

33

38 PTA

<0.1

2.5-3.5

6

Bal.

–

–

–

1.8-2.4

–

<3

–

40

54 PTA

0.5-0.7

3.5-4.5

15-17

Bal.

2-4

–

–

3-4

–

<4

Cu: 2-3

56-61

55 PTA

0.4-0.6

3.5-4.5

12-14

Bal.

–

–

–

2.5-3.5

–

<4

–

50-55

56 PTA

0.25

3.2

7.5

Bal.

–

–

–

1.8

–

<4

–

40

57 PTA

0.9-1.1

4

15-17

Bal.

–

–

–

3.2

–

<4

–

58-60

58 PTA

0.75

4.3

15

Bal.

–

–

–

3.1

–

<4

–

50-52

59 PTA

<0.1

3

–

Bal.

–

–

–

3

–

<2

–

50-52

61 PTA

<0.1

3

–

Bal.

–

–

–

3

–

<2

–

50-52

62 PTA

<0.1

3

–

Bal.

–

–

–

3

–

<2

–

50-52

63 PTA

0.25

3.2

7.5

Bal.

–

–

–

1.8

–

<2.5

–

40

65 PTA

0.75

4.3

15

Bal.

–

–

–

3.1

–

<4

–

50-52

66 PTA

0.4

<0.1

15-17

Bal.

–

–

–

3

–

<4

SC: 10-15

50

67 PTA

0.02

3

–

Bal.

–

–

–

3

–

<2

–

50-52

68 PTA

0.02

3

–

Bal.

–

–

–

3

–

<2

–

50

71 PTA

<0.1

3

–

Bal.

–

–

–

3

–

<45

–

50-55

72 PTA

<0.1

3

–

Bal.

–

–

–

3

–

<45

–

50-55

73 PTA

<0.1

3

–

Bal.

–

–

–

3

–

<45

–

50-55

74 PTA

<0.1

<0.1

–

Bal.

–

–

–

3.5

–

<5

–

50

77 PTA

<0.1

3

–

Bal.

–

–

–

3

–

<45

–

50-55

79 PTA

0.9-1.1

4

15-17

Bal.

–

–

–

3.2

–

<4

–

58-60

84 PTA

–

4.1

15-17

Bal.

–

–

–

3.2

–

<4

–

33

85 PTA

0.75

4.3

15

Bal.

–

–

–

3.1

–

<4

–

50-52

93 PTA

<0.1

3

–

Bal.

–

–

–

3

–

<2

–

50-52

110 PTA

0.25

3.2

7.5

Bal.

–

–

–

1.8

–

<4

–

40

401 PTA

<0.1

–

20-24

Bal.

8-9

3.5

<5

–

<4

<5

–

55-56

411 PTA

<0.1

–

20-24

Bal.

8-9

3.5

<5

–

<4

<5

–

55-56

470 PTA

–

2.75

4

Bal.

–

–

–

1

–

–

Andere: 5

33

625 PTA

0.05

–

21

Bal.

9,2

3.5

–

–

–

3

–

210 HV